ISO 8502-2-2005 涂覆油漆和相关产品前钢材衬底的预处理.表面清洁度的评定试验.第2部分_洁净表面氯化物的测定.pdf

标准号：ISO 8502-2-2005
实施状态：作废
中文名称：涂覆油漆和相关产品前钢材衬底的预处理.表面清洁度的评定试验.第2部分:洁净表面氯化物的测定
英文名称：Preparation of steel substrates before application of paints and related products - Tests for the assessment of surface cleanliness - Part 2: Laboratory determination of chloride on cleaned surfaces
发布日期：2005-10
被替代标准：ISO 8502-2-2017
代替标准：ISO 8502-2-1992;ISO/FDIS 8502-2-2005
采用标准：DIN EN ISO 8502-2-2006,IDT;BS EN ISO 8502-2-2006,IDT;GB/T 18570.2-2009,IDT;EN ISO 8502-2-2005,IDT;NF T35-502-2-2006,IDT;SN EN ISO 8502-2-2006,IDT;OENORM EN ISO 8502-2-2006,IDTN-EN ISO 8502-2-2006,IDTN-EN ISO 8502-2-2006,IDT;UNE-EN ISO 8502-2-2006,IDT
起草单位：ISO/TC 35
标准简介：This part of ISO 8502 describes a method for the determination of chloride-containing salts that are readily soluble in water and are present on a steel surface. The method is also applicable to previously coated surfaces. It will normally be used in a laboratory using washings sampled from surfaces on site.
The method is applicable to the determination of salts that have been deposited on the steel surface before, during or after the cleaning operations.
NOTE 1  Although the procedure for chloride determination is generally accurate, the overall precision of the method is limited by uncertainties in the sampling procedure. In addition, traces of iron chloride at the bottom of pits are difficult to extract into the sample.
The test method is not applicable to surfaces treated with chromate, nitrite or amine, which are commonly used as inhibitors in the water when wet blast-cleaning. This is because a chromate concentration of 10 mg/l or greater or a nitrite concentration of 20 mg/l or greater in the wash water interferes with the determination of the chloride. Also the amine inhibitors can form a hydroxide boundary layer (not water soluble) over the substrate and prevent the water from contacting the underlying salt for its removal.
An iron(lll) ion concentration of 10 mg/l also interferes with the determination, but the iron(lll) ions are concentrated in the rust deposits, which are removed from the test solution by filtration.
NOTE 2  The performance of a paint system is affected by the amount of soluble chloride remaining on the surface. The acceptable level of this contamination is related to the service conditions. For further information regarding levels of water-soluble salt contamination see ISO/TR 15235 <up[1]>.
文件格式：PDF
文件大小：151.99KB
文件页数：14
（以上信息更新时间为：2019-11-22）