ISO 14577-1-2002 金属材料.硬度和材料参数的仪器压痕试验.第1部分_试验方法.pdf

标准号：ISO 14577-1-2002
实施状态：作废
中文名称：金属材料.硬度和材料参数的仪器压痕试验.第1部分:试验方法
英文名称：Metallic materials - Instrumented indentation test for hardness and materials parameters - Part 1: Test method
发布日期：2002-10
被替代标准：ISO 14577-1-2015
代替标准：ISO/TR 14577-1995;ISO/FDIS 14577-1-2002
采用标准：DIN 50359-1-1997,MOD;DIN EN ISO 14577-1-2003,IDT;BS EN ISO 14577-1-2002,IDT;GB/T 21838.1-2008,MOD;EN ISO 14577-1-2002,IDT;NF A03-155-1-2003,IDT;SN EN ISO 14577-1-2003,IDT;OENORM EN ISO 14577-1-2003,IDTN-EN ISO 14577-1-2005,IDT;UNE-EN ISO 14577-1-2005,IDT
起草单位：ISO/TC 164
标准简介：This part of ISO 14577 specifies the method of instrumented indentation test for determination of hardness and other materials parameters for the three ranges given in Table 1.
The macro and micro range are distinguished by the test forces in relation to the indentation depth.
Attention is drawn to the fact that the micro range has an upper limit given by the test force (2 N) and a lower limit given by the indentation depth of 0,2 um.
The determination of hardness and other materials parameters is given in annex A.
At high contact pressures, damage to the indenter is possible. For this reason in the macro range, hardmetal indenters are often used. For test pieces with very high hardness and modulus of elasticity the influence of indenter deformation on the test result should be taken into account.
NOTE      This test method can also be applied to thin metallic and non-metallic coatings and non-metallic materials. In this case the specifications in the relevant standards should be taken into account (see also 6.3).