标准号：ISO 9015-2-2003
实施状态：作废
中文名称：金属材料焊接的破坏性试验.硬度试验.第2部分:焊接件的显微硬度试验
英文名称：Destructive tests on welds in metallic materials - Hardness testing - Part 2: Microhardness testing of welded joints
发布日期：2003-11
被替代标准：ISO 9015-2-2016
代替标准：ISO/FDIS 9015-2-2003
采用标准：DIN 50163-10-1995,IDT;DIN EN ISO 9015-2-2010,IDT;FprEN ISO 9015-2-2010,IDT;A89-204-2PR,IDT;OENORM EN ISO 9015-2-2010,IDT
起草单位：ISO/TC 44
标准简介：This part of ISO 9015 specifies microhardness tests on transverse sections of welded joints of metallic materials with high hardness gradients. It covers Vickers hardness tests in accordance with ISO 6507-1, normally with test loads of 0,98 N to less than 49 N (HV 0,1 to less than HV 5).
NOTE Testing should be carried out to ensure that the highest and/or the lowest level of hardness of both parent materials (in the case of dissimilar materials both parent materials) and weld metal is determined.
This part of ISO 9015 does not cover hardness testing of welds with loads of 49,03 N and above, covered by ISO 9015-1.
This part of ISO 9015 is not applicable to hardness testing of very narrow welds, e.g. those typically produced by laser and electron beam welding, covered by ISO 22826.